Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates

  • Deze norm is ingetrokken sinds 01-08-2017

50,60 61,23 Incl BTW

Over deze norm

Status Ingetrokken
Aantal pagina's 9
Gepubliceerd op 01-08-2017
Taal Engels

1.1 This test practice defines the procedure for determination of the tensile strength of a tapered or stepped joint of polymer matrix composite materials. It is applicable to secondary bonded or co-bonded laminates with either unidirectional plies or woven fabric reinforcements. The materials to be bonded may be different material systems. In the bondline, a separate adhesive material may or may not be used (example: adhesives may be used with a prepreg system or may not be used with a wet lay-up repair system). The range of acceptable test laminates and thicknesses is described in 8.2.1.

1.2 This practice supplements Test Method D3039/D3039M for tensile loading. Several important test specimen parameters (for example, joint length, ply overlaps, step depth, and taper ratio) are not mandated by this practice, however, these parameters are required to be specified and reported to support repeatable results.

1.3 Unidirectional (0° ply orientation) tape composites, textile composites, as well as multidirectional composite laminates, can be tested.

1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard.

1.4.1 Within the text the inch-pound units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Details

Engelse titel Standard Practice for Tensile Properties of Tapered and Stepped Joints of Polymer Matrix Composite Laminates
Vervangen door

Winkelwagen

Subtotaal:

Ga naar winkelwagen