ISO/DIS 4589-3:2016 en

Kunststoffen - Bepaling van de brandgedrag met de zuurstofindex - Deel 3: Beproeving bij verhoogde temperatuur

  • Deze norm is niet direct leverbaar vanuit de NEN-shop.
    Wilt u dit product bestellen neemt u dan contact op met NEN-klantenservice: (015) 2 690 391 of klantenservice@nen.nl

Over deze norm

Status Ontwerp
Aantal pagina's 24
Commissie Aanstekers
Gepubliceerd op 18-02-2016
Taal Engels
This part of ISO 4589 specifies methods for determining the minimum volume fraction of oxygen, in a mixture with nitrogen, that will support combustion of small vertical test specimens under specified test conditions over a range of temperatures between 25 °C and 150 °C. The range of temperatures is typically between 40 °C and 150 °C. The results are defined as temperature index values at the test temperature, which is typical of the practical temperature that a plastic material may experience in an overheated service situation. Methods are provided for testing materials that are self-supporting at the test temperature in the form of vertical bars or sheet up to 10,5 mm thick. However, they are not applicable to form V which requires supporting frame as defined in Table 2 of Part 2. These methods are suitable for solid, laminated or cellular materials characterized by an apparent density 100 kg/m3 or greater. The methods may also be applicable to some cellular materials having an apparent density of less than 100 kg/m3. A method is provided for testing flexible sheet or film materials while supported vertically. This part of ISO 4589 also includes a method (see Annex A) for determining the temperature at which the oxygen index of small vertical test specimens in air is 20,9 % under specified test conditions. The temperature at which this occurs is defined as the flammability temperature (FT) and the method is limited to the determination of temperatures less than 400 °C. The method is not applicable to materials having an oxygen index of < 20,9 %. Results obtained in accordance with this part of ISO 4589 is not applicable to describe or appraise the fire hazard presented by a particular material or shape under actual fire conditions, unless used as one element of a fire risk assessment which takes into account all of the factors which are pertinent to the assessment of the fire hazard of a particular application for the material.

Details

ICS-code 13.220.40
83.080.01
Nederlandse titel Kunststoffen - Bepaling van de brandgedrag met de zuurstofindex - Deel 3: Beproeving bij verhoogde temperatuur
Engelse titel Plastics - Determination of burning behaviour by oxygen index - Part 3: Elevated-temperature test