This part of ISO 75 specifies three methods, using different values of constant flexural stress, that can be used for the determination of the temperature of deflection under load of plastics (including filled plastics and fibre-reinforced plastics in which the fibre length, prior to processing, is up to 7,5 mm) and ebonite: - method A, using a flexural stress of 1,80 MPa; - method B, using a flexural stress of 0,45 MPa; - method C, using a flexural stress of 8,00 MPa. The standard deflection, Δs, used to determine the temperature of deflection under load corresponds to a flexural-strain increase, Δef, defined in this part of ISO 75. The initial flexural strain due to the loading of the specimen at room temperature is neither specified nor measured in this part of ISO 75. The ratio of this flexural-strain increase to the initial flexural strain depends on the modulus of elasticity, at room temperature, of the material under test. This method is, therefore, only suitable for comparing the temperatures of deflection of materials with similar room-temperature elastic properties.
|Nederlandse titel||Kunststoffen - Bepaling van de vervormingstemperatuur onder belasting - Deel 2: Kunststoffen en eboniet|
|Engelse titel||Plastics - Determination of temperature of deflection under load - Part 2: Plastics and ebonite|